Legowon	Standard Stréibicher, mm	Resistenz, ω / m	Strang Duerchmiesser nominell, mm	Meter pro Kilo
NICR 80/20	18 × 0,544 + 1 × 0,574	0,252-0278	2.67	26
NICR 80/20	19 × 0.61	0.205-0.250	3.05
NICR 80/20	18 × 0,523 + 1 × 0,574	0,271-0.299	2.67	30
NICR 80/20	19 × 0,574	0,227-0.251	2.87	25
NICR 80/20	36 × 0.385 + 1 × 0,45	0.265-0.293	2.76	26
NICR 60/15	19 × 0.508	0,286-0,318	2.54
NICR 60/15	18 × 0,523 + 1 × 0,574	0,276-0.305	2.76	30
Ni200 / NI201	19 × 0,574	0,019-0.021	2.87	21

N6	Chromel C, NI 60, N6, Hai-Niter, Tophet C, Resistohthm 60, Connifer II,
	Elektroyony, Nichrome, Alloy C, NI 6, MWS-675, Stablohm 675
N7	NI 70, Chromel 70/30, N7, hymemco, Hai-Niter 70, Balco, Tophet 30,
	Resistthm 70, Cronix 70, Stablohm 710
N8	Chromel A, NI 80, N8, Nichrom V, Hai-Niter 80, tophet a, resistthm
	80, Cronix 80, Protoyy, NI 8, Legierung A, MWS-650, Stablohm 650

Eegeschafte / Grad		Cr20ni80	Cr30ni70	Cr15ni60	Cr20ni35	Cr20ni30
Haaptweineschkompositioun	Ni	Rescht	Rescht	55.0,61.0	34.0-37.0	30,0-34.0
	Cr	20.0-23.0	28.0-31.0	15,0-18.0	18.0-21.0	18.0-21.0
	Fe	≤ 1.0	≤ 1.0	Rescht	Rescht	Rescht
Max. kontinuéierlech Service Temp. vum Element		1200	1250	1150	1100	1100
Resistivitéit um 20oC (μ ω · m)		1.09	1.18	1.12	1.04	1.04
Dicht (g / cm3)		8.4	8.1	8.2	7.9	7.9
Thermesch Verwaltungsimitéit (kj / m · h · oc)		60.3	45..2	45..2	43.8	43.8
Koeffizient vun Linnen Expansioun (α × 10-6 / OC)		18	17	17	19	19
Schmelzen Punkt (ongeféier.) (OC)		1400	1380	1390	1390	1390
Verlängeren op der Rupture (%)		> 20	> 20	> 20	> 20	> 20
Mikrographesch Struktur		austenit	austenit	austenit	austenit	austenit
Magnéitesch Eegeschaften		nonmagnetesch	nonmagnetesch	nonmagnetesch	nonmagnetesch	nonmagnetesch